Aluminum-coated step index multimode silica fibers CCR 1.1 (High OH)
Aluminum-coated step index multimode optical fibers (Core/Clad Ratio 1.1) have all the benefits of silica-silica fibers. Additional significant improvements include increased mechanical strength and greater fatigue resistance compared to non-hermetic and polymer-clad fibers (PCS). Their transmittance covers a spectral range of 250 to 1200 nm, and also remains stable in corrosive chemicals that normally react to silica glass. The temperature range is from -196C to +400C .

FEUTURES:
  • Greatly enhanced resistance to high power laser radiation.
  • Higher core-to-clad ratio and enlarged NA optimized for coupling to high-energy lasers.
  • Better fiber cooling due to the heat-conducting metal coating.
  • Excellent mechanical strength and flexibility compared to polymer coated fibers.
  • The metal coating can be soldered and will not outgas.

 

Aluminum-coated fibers ОК-100/110AL ОК-150/165AL ОК-200/220AL ОК-300/330AL ОК-400/440AL ОК-600/660AL ОК-800/880AL ОК-1000/1100AL
Fiber type MM MM MM MM MM MM MM MM
Index profile Step Step Step Step Step Step Step Step
Core diameter, µm 100 ± 2 150 ± 3 200 ± 4 300 ± 6 400 ± 8 600 ± 12 800 ± 15 1000 ± 20
Clad diameter, µm 110 ± 3 165 ± 4 220 ± 5 330 ± 10 440 ± 12 660 ± 15 880 ± 20 1100 ± 40
Coating diameter, µm 150 ± 8 210 ± 12 300 ± 15 450 ± 25 565 ± 25 860 ± 30 1110 ± 40 1410 ± 60
Cladding offset, % < 2
Coating offset, % < 5
Attenuation at 800/1300 nm (High OH) the loss spectrum in the long wavelength region ( > 1um) is higher than that of the material the loss spectrum is close to the material loss spectrum
Wavelength range, nm (High OH) 250 - 1100 250 - 1200
Coating material Aluminium
Core material Pure syntetic silica (High OH)
Clad material Doped silica
Numerical Aperture (NA) 0.22 ± 0.02
Short-term bending radius 60 times the fiber diameters
Long-term bending radius 120 times the fiber diameters
Proof test, kpsi 100
Min operating temperature, C -196
Max operating temperature, C 400
If you are interested in purchasing our products you can write to us!